Soy oil fatty acid short oil alkyd resin
|
|
ITEM
|
COLOR (Fe-Co,60%)
|
NV (±2,%)
|
VISCOSITY (25°C)
|
OH VALUE (±10,固體)
|
PROPERTIES & APPLICATION
|
|
GL1100C
|
≤3
|
70
|
30-60S(格式,60%)
|
120
|
High gloss, fullness, high hardness, good adhesion, flexibility, used for amino-baking coatings, acid curing paint, lacquer.
|
|
GL1100D
|
≤3
|
70
|
130-180S(格式,60%)
|
100
|
Quick drying, high hardness, easy to burnish, standard for high-grade PU wood primer, dumb smooth varnish.
|
|
GL1100F
|
≤5
|
70
|
18-50S(格式,60%)
|
110
|
Quick drying, high hardness, easy to burnish, amino paint, general PU wood primer, used for NC lacquer.
|
|
GL1100T
|
≤3
|
70
|
150-220S(格式,60%)
|
110
|
Quick drying, high viscosity, high hardness, easy to burnish, used for PU wood primer, be bored with child.
|
|
GL1108
|
≤3
|
70
|
130-190S(格式,60%)
|
110
|
Fast drying speed, grinding resistance, long period of activation, paint film mechanical properties, suitable for PU primer, dumb smooth varnish.
|
|
GL1122
|
≤8
|
70
|
25-68S(格式,60%)
|
*
|
Resistance to impact, pigment dispersion, used for bike of the lacquer that bake.
|
|
GL1165
|
≤3
|
70
|
65-145S(格式,60%)
|
150
|
Good solvent resistance, prevent bit bottom, used for high fullness dumb smooth paint and solvent resistant primer.
|
|
GL1166
|
≤3
|
70
|
20-50S(格式,60%)
|
110
|
Low viscosity, good fullness, high gloss, used to highlight the PU paint wood coatings, hand.
|
|
GL1166D
|
≤3
|
70
|
30-80S(格式,60%)
|
110
|
High viscosity, easy to extinction, for PU wood primer, matte paint.
|
|
GL1167
|
≤3
|
60
|
19-40S(格式,50%)
|
100
|
Quick drying, high hardness, easy to burnish, easy to extinction, for PU wood matte paint and primer.
|
|
GL1177
|
≤3
|
70
|
90-150S(格式,60%)
|
110
|
Fast drying speed, easy to burnish, activation period is long, can add appropriately drier, used for PU primer, dumb smooth varnish.
|
|
GL1177B
|
≤3
|
70
|
35000-50000mpa.s
|
120
|
Quick drying, good polishing, resistance to dilute, subsidence prevention function, used in PU primer and topcoat.
|
|
GL1177D
|
≤5
|
70
|
80000-120000mpa.s
|
115
|
Quick drying, high viscosity, high hardness, good polishing, used in PU primer and topcoat.
|